(請教)PET物料在試模中的困惑

colin20001

我這里有個新產品用到PET的這只料.在試模生產中發現,如果使用高模溫時成型周期就要很長,且容易粘模,如果采用較低的模溫,則成品表面出現"白霧"類似不飽模.(烘料130度5小時)

colin20001

我靠!我滿怀希望的打開貼子看到的是妳說的廢話,我倒阿`~~~~

colin20001

哪位用過,發表一下高見,先謝了.

cyw59

我见过矿泉水瓶的胚管用PET，具体使用注意的事项不知道[em08][em08][em08][em08]

lc

PET用来注射的好像没见过.

colin20001

高模溫,高射速,成型后表面發白,放置2天后有所改善.模溫以及成型條件不當易粘模.公母模都有粘,這是很少見的問題.持續試模中,如有突破行進展我將發表.

colin20001

Process for molding 107056-25-100
*        Must use hot oil mold heater to heat both mold halves to 320 degrees
F.
*        First stage injection time is 2.5 seconds at 750 PSI.
*        Second stage holding time is 5 seconds at 400 PSI.
*        Cure time must be 35 seconds minimum.
*        Must have at least 35 seconds to ensure part transfer from A side to
B side
*        Stock temperature:
*        Rear zone 530 degrees F
*        Middle zone 560 degrees F
*        Front zone 570 degrees F
*        Nozzle temperature 575 degrees F
*        Material must dry for a minimum of 3 hours.

Additional notes:  Mold temperature is very important.  Cannot vary too much.  Must make sure material is dry. Very important.

jutonglei

我也不知道呀

kinage

建議樓主先了解一下工程塑料pet的特性,在試模的時候找出最佳壓力,溫度,以及注射成型凝固時間.看是不是要加點什麼其它的料.

yj10377

倒是见过用来吹塑做瓶，其没注塑那么复杂。

vagabond

楼主,请教一下,PET的中文名是??有些什么特性?

anntong

<P>我做過,化妝品的.用熱流道做的.成型工藝表.我找一下.</P>